Scientists Unravel Mechanism of Ion and Electron Migration in Composite Solid Electrolytes (Chemistry)

Scientists from the Advanced lithium-ion Battery Engineering Laboratory, Ningbo Institute of Materials Technology and Engineering (NIMTE) of the Chinese Academy of Sciences (CAS), revealed the mechanism in of ion and electron migration in composite solid electrolytes (CSEs) through the conductive atomic force microscopy (c-AFM), which facilitates the design of high-performance solid electrolytes. The study was published in Energy Storage Materials

Compared with the traditional lithium-ion (Li-ion) battery, the solid-state battery with solid materials as electrolyte has higher energy density and safety. As a combination of inorganic solid electrolytes (ISEs) and solid polymer electrolytes (SPEs), CSEs showed excellent contact with electrodes and high ionic conductivity. However, the role of inorganic particles and migration of Li-ions is still controversial. 

To address this issue, Dr. SHEN Cai and his colleagues at NIMTE prepared Li7La3Zr2O12-polyethylene oxide (LLZO-PEO) CSEs with different ratios of LLZO, i.e., 0, 50, 75 wt. %. The c-AFM was equipped with a quantitative nano-mechanical measurement module (QNM), which collected the topography and sample current while obtaining mechanical information. By virtue of the c-AFM, the effects of temperature and LLZO content on the migration of ion and electron in CSEs were investigated. 

At low temperatures, Li-ions can only migrate along the amorphous PEO regardless of LLZO content. The addition of LLZO lead to the formation of PEO amorphous region at the interface between LLZO and PEO, reducing the crystallinity and glass transition temperature of PEO.  

At high temperatures, Li-ions mainly migrated along the amorphous PEO when a small amount (i.e., 0 and 50 wt. %) of LLZO particles was added. With the increase of LLZO content (75 wt. %), LLZO particles formed a continuous ionic conductive network in the PEO matrix, and lithium ions migrated through LLZO particles.  

The as-prepared electrolyte showed dominant Li-ion migration, which was three orders of magnitude higher than the electronic current. In addition, the electronic current from PEO is much larger than that of LLZO, which indicates that the addition of LLZO can improve the electronic insulation of CSEs.  

Furthermore, due to the high modulus and excellent insulation properties of LLZO, the addition of LLZO into the electrolytes is expected to inhibit the growth of li dendrites in lithium anodes. 

This study revealed the influence of inorganic particle content and working temperature on the performance of CSEs, which provides novel insights into the design and development of CSEs for solid-state batteries.


Reference: Cai Shen, Yunbo Huang, Jingru Yang, Minjing Chen, Zhaoping Liu, Unraveling the mechanism of ion and electron migration in composite solid-state electrolyte using conductive atomic force microscopy, Energy Storage Materials, Volume 39, 2021, Pages 271-277, ISSN 2405-8297, https://doi.org/10.1016/j.ensm.2021.04.028. (https://www.sciencedirect.com/science/article/pii/S2405829721001707)


Provided by Chinese Academy of Sciences

Leave a Reply

Fill in your details below or click an icon to log in:

WordPress.com Logo

You are commenting using your WordPress.com account. Log Out /  Change )

Google photo

You are commenting using your Google account. Log Out /  Change )

Twitter picture

You are commenting using your Twitter account. Log Out /  Change )

Facebook photo

You are commenting using your Facebook account. Log Out /  Change )

Connecting to %s